Minimal Match — 54.9% match
based on chemical composition and mechanical property overlap.
UNS C27000 and UNS C28000 are both brass grades.
Both fall under the Brass Alloys category.
UNS C27000 is defined under Unified Numbering System (UNS), originating from United States, while UNS C28000 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C27000 vs UNS C28000 is a 82.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 54.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C27000
UNS C28000
Yield Strength
~180-230 MPa (H02 half-hard)
~145 MPa (O61 annealed)
Tensile Strength
~400-450 MPa (H02 half-hard)
~372 MPa (O61 annealed)
Elongation
~25-45% (H02 half-hard)
~50% (O61 annealed)
Note
Yellow brass, values for H02 half-hard temper
Muntz metal, values for O61 annealed condition
Can UNS C27000 Be Substituted With UNS C28000?
UNS C27000 and UNS C28000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C27000 and UNS C28000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can UNS C27000 be substituted with UNS C28000?
UNS C27000 and UNS C28000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.