AISI 8620 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

AISI 8620 and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. AISI 8620 is typically used for used for gears, shafts, sprockets, pinions, bushings, and transmission components., while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. AISI 8620 is defined under AISI, originating from United States, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, AISI 8620 vs IS 1570 (Part 7) 10Cr36Mo10H is a 53.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With AISI 8620:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
53.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property AISI 8620 IS 1570 (Part 7) 10Cr36Mo10H
Standard AISI IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.18-0.23 <=0.15
Mn (%) 0.70-0.90 0.30-0.60
Si (%) 0.15-0.35 0.25-1.0
Ni (%) 0.40-0.70 Not specified
Cr (%) 0.40-0.60 8.00-10.00
Mo (%) 0.15-0.25 0.90-1.10
P (%) 0.035 max <=0.040
S (%) 0.040 max <=0.030
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 8620 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength 750-980 MPa 410-560 MPa
Yield Strength 550-780 MPa >=135 MPa (0.2 % proof stress)
Elongation 12-18% >=20%
Hardness 200-280 HB Not specified
Condition Not specified Pipes, A, thickness - (first row of Table 3)
Typical Applications
AISI 8620
Used for gears, shafts, sprockets, pinions, bushings, and transmission components.
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can AISI 8620 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
AISI 8620 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
AISI 8620
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6600–6900 mm (259.84–271.65 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
AISI 8620
2 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 8620 and IS 1570 (Part 7) 10Cr36Mo10H?
AISI 8620 specifies Ni which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for AISI 8620.
Can AISI 8620 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
AISI 8620 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.