ASTM A681 D2 vs GB/T 1299 4Cr5MoSiV1

Minimal Match — 41.9% match based on chemical composition and mechanical property overlap.

ASTM A681 D2 (ASTM A681:2008) and GB/T 1299 4Cr5MoSiV1 (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 D2 is typically used for blanking dies, punches, drawing dies, forming tools, while GB/T 1299 4Cr5MoSiV1 is commonly used for die casting dies, forging dies, extrusion tools. ASTM A681 D2 is defined under ASTM International, originating from United States, while GB/T 1299 4Cr5MoSiV1 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A681 D2 vs GB/T 1299 4Cr5MoSiV1 is a 62.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 41.9%.

Frequently Compared With ASTM A681 D2:
DIN EN ISO 4957 1.2379 EN ISO 4957 1.2316 EN ISO 683-17 100Cr6 DIN EN ISO 4957 1.2344 AISI 52100 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV GB/T 1299 3Cr2W8V GOST 5950 4H5MFS GOST 5950 4H5MFS1 IS 3748 103T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
62.9%
MECHANICAL MATCH
0%
OVERALL
41.9%
Specifications
Property ASTM A681 D2 GB/T 1299 4Cr5MoSiV1
Standard ASTM A681:2008 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 1.40-1.60 0.32–0.45
Mn (%) 0.10-0.60 0.20–0.50
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) 0.10-0.60 0.80–1.20
Cr (%) 11.00-13.00 4.75–5.50
V (%) 0.50-1.10 0.80–1.20
Mo (%) 0.70-1.20 1.20–1.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 D2 GB/T 1299 4Cr5MoSiV1
Hardness <=255 HB Not specified
Condition Annealed (maximum Brinell hardness) Not specified
Hardness HRC (hardened) Not specified 42–54
Hardness HB (annealed) Not specified ≤235
Typical Applications
ASTM A681 D2
Blanking dies, punches, drawing dies, forming tools
GB/T 1299 4Cr5MoSiV1
Die casting dies, forging dies, extrusion tools
Key Differences
Can ASTM A681 D2 Be Substituted With GB/T 1299 4Cr5MoSiV1?
ASTM A681 D2 and GB/T 1299 4Cr5MoSiV1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 D2
Round Bar → (19 listings)
Diameter: 70–120 mm (2.76–4.72 in)
Length: 2600–6900 mm (102.36–271.65 in)
Flat Bar → (3 listings)
Thickness: 30–30 mm (1.18–1.18 in)
Width: 150–150 mm (5.91–5.91 in)
Length: 1000–2500 mm (39.37–98.43 in)
GB/T 1299 4Cr5MoSiV1
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2700–4100 mm (106.3–161.42 in)
On M-EX Right Now
ASTM A681 D2
22 active listings and RFQs →
GB/T 1299 4Cr5MoSiV1
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 D2 and GB/T 1299 4Cr5MoSiV1?
ASTM A681 D2 specifies P, S which are not specified for GB/T 1299 4Cr5MoSiV1.
Can ASTM A681 D2 be substituted with GB/T 1299 4Cr5MoSiV1?
ASTM A681 D2 and GB/T 1299 4Cr5MoSiV1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.