ASTM A681 H13 vs GB/T 1299 4Cr5MoSiV1

Strong Match — 96.4% match based on chemical composition and mechanical property overlap.

ASTM A681 H13 (ASTM A681:2008) and GB/T 1299 4Cr5MoSiV1 (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 H13 is typically used for die casting dies, extrusion dies, forging dies, hot stamping, while GB/T 1299 4Cr5MoSiV1 is commonly used for die casting dies, forging dies, extrusion tools. ASTM A681 H13 is defined under ASTM International, originating from United States, while GB/T 1299 4Cr5MoSiV1 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A681 H13 vs GB/T 1299 4Cr5MoSiV1 is a 94.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 96.4%.

Frequently Compared With ASTM A681 H13:
GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2344 EN ISO 683-17 100Cr6 GOST 5950 4H5MFS GOST 5950 4H5MFS1 GOST 5950 3H2W8F GB/T 1299 3Cr2W8V EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 AISI 52100 IS 3748 103T3
Match Breakdown
CHEMISTRY MATCH
94.6%
MECHANICAL MATCH
100%
OVERALL
96.4%
Specifications
Property ASTM A681 H13 GB/T 1299 4Cr5MoSiV1
Standard ASTM A681:2008 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.32-0.45 0.32–0.45
Mn (%) 0.20-0.60 0.20–0.50
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) 0.80-1.25 0.80–1.20
Cr (%) 4.75-5.50 4.75–5.50
V (%) 0.80-1.20 0.80–1.20
Mo (%) 1.10-1.75 1.20–1.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 H13 GB/T 1299 4Cr5MoSiV1
Hardness <=235 HB Not specified
Condition Annealed (maximum Brinell hardness) Not specified
Hardness HRC (hardened) Not specified 42–54
Hardness HB (annealed) Not specified ≤235
Typical Applications
ASTM A681 H13
Die casting dies, extrusion dies, forging dies, hot stamping
GB/T 1299 4Cr5MoSiV1
Die casting dies, forging dies, extrusion tools
Key Differences
Can ASTM A681 H13 Be Substituted With GB/T 1299 4Cr5MoSiV1?
ASTM A681 H13 and GB/T 1299 4Cr5MoSiV1 overlap closely enough on chemistry and mechanical properties that GB/T 1299 4Cr5MoSiV1 is often considered as a substitute for ASTM A681 H13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
ASTM A681 H13
Round Bar → (26 listings)
Diameter: 65–100 mm (2.56–3.94 in)
Length: 2500–6500 mm (98.43–255.91 in)
Flat Bar → (3 listings)
Thickness: 40–40 mm (1.57–1.57 in)
Width: 200–200 mm (7.87–7.87 in)
Length: 700–1600 mm (27.56–62.99 in)
GB/T 1299 4Cr5MoSiV1
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2700–4100 mm (106.3–161.42 in)
On M-EX Right Now
ASTM A681 H13
29 active listings and RFQs →
GB/T 1299 4Cr5MoSiV1
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 H13 and GB/T 1299 4Cr5MoSiV1?
ASTM A681 H13 specifies P, S which are not specified for GB/T 1299 4Cr5MoSiV1.
Can ASTM A681 H13 be substituted with GB/T 1299 4Cr5MoSiV1?
ASTM A681 H13 and GB/T 1299 4Cr5MoSiV1 overlap closely enough on chemistry and mechanical properties that GB/T 1299 4Cr5MoSiV1 is often considered as a substitute for ASTM A681 H13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.