ASTM A240/A240M S20103 vs ASTM A959 201LN

Close Alternative — 83.6% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S20103 (ASTM A240/A240M:2025) and ASTM A959 201LN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S20103 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 201LN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S20103 is defined under ASTM International, originating from United States, while ASTM A959 201LN is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S20103 vs ASTM A959 201LN is a 83.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.6%.

Frequently Compared With ASTM A240/A240M S20103:
IS 1570 (Part 7) 12Cr12MoVH ASTM A959 201L GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
83.6%
MECHANICAL MATCH
No shared data
OVERALL
83.6%
Specifications
Property ASTM A240/A240M S20103 ASTM A959 201LN
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.03
Mn (%) 5.50-7.50 6.4-7.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=0.75 <=1.00
Cr (%) 16.0-18.0 16.0-17.5
Ni (%) 3.5-5.5 4.0-5.0
N (%) <=0.25 0.10-0.25
Cu (%) Not specified <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S20103 ASTM A959 201LN
Tensile Strength >=655 MPa Not specified
Yield Strength >=260 MPa Not specified
Elongation >=40% Not specified
Hardness <=217 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S20103
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 201LN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S20103 Be Substituted With ASTM A959 201LN?
ASTM A240/A240M S20103 and ASTM A959 201LN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S20103
0 active listings and RFQs →
ASTM A959 201LN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S20103 and ASTM A959 201LN?
ASTM A959 201LN specifies Cu which is not specified for ASTM A240/A240M S20103.
Can ASTM A240/A240M S20103 be substituted with ASTM A959 201LN?
ASTM A240/A240M S20103 and ASTM A959 201LN are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.