ASTM A240/A240M S30100 vs ASTM A240/A240M S32100

Close Alternative — 83.8% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S30100 (ASTM A240/A240M:2025) and ASTM A240/A240M S32100 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S30100 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A240/A240M S32100 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A240/A240M S30100 is defined under ASTM International, originating from United States, while ASTM A240/A240M S32100 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S30100 vs ASTM A240/A240M S32100 is a 75.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a close alternative overall at 83.8%.

Frequently Compared With ASTM A240/A240M S30100:
IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
75.7%
MECHANICAL MATCH
100%
OVERALL
83.8%
Specifications
Property ASTM A240/A240M S30100 ASTM A240/A240M S32100
Standard ASTM A240/A240M:2025 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.08
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.75
Cr (%) 16.0-18.0 17.0-19.0
Ni (%) 6.0-8.0 9.0-12.0
N (%) <=0.10 <=0.10
Ti (%) Not specified <=0.70
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S30100 ASTM A240/A240M S32100
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa
Elongation >=40% >=40%
Hardness <=217 HB <=217 HB
Condition Plate, sheet and strip; yield by 0.2 percent offset Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A240/A240M S30100
Pressure vessels and general applications (plate, sheet and strip)
ASTM A240/A240M S32100
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A240/A240M S30100 Be Substituted With ASTM A240/A240M S32100?
ASTM A240/A240M S30100 and ASTM A240/A240M S32100 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S30100
0 active listings and RFQs →
ASTM A240/A240M S32100
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S30100 and ASTM A240/A240M S32100?
ASTM A240/A240M S32100 specifies Ti which is not specified for ASTM A240/A240M S30100.
Can ASTM A240/A240M S30100 be substituted with ASTM A240/A240M S32100?
ASTM A240/A240M S30100 and ASTM A240/A240M S32100 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.