ASTM A240/A240M S31726 vs ASTM A959 317LM

Strong Match — 93.1% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S31726 (ASTM A240/A240M:2025) and ASTM A959 317LM (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S31726 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 317LM is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S31726 is defined under ASTM International, originating from United States, while ASTM A959 317LM is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S31726 vs ASTM A959 317LM is a 93.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.1%.

Frequently Compared With ASTM A240/A240M S31726:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
No shared data
OVERALL
93.1%
Specifications
Property ASTM A240/A240M S31726 ASTM A959 317LM
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=0.75 <=1.00
Cr (%) 17.0-20.0 18.0-20.0
Ni (%) 13.5-17.5 13.5-17.5
Mo (%) 4.0-5.0 4.0-5.0
N (%) 0.10-0.20 <=0.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S31726 ASTM A959 317LM
Tensile Strength >=550 MPa Not specified
Yield Strength >=240 MPa Not specified
Elongation >=40% Not specified
Hardness <=223 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S31726
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 317LM
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A240/A240M S31726 Be Substituted With ASTM A959 317LM?
ASTM A240/A240M S31726 and ASTM A959 317LM overlap closely enough on chemistry and mechanical properties that ASTM A959 317LM is often considered as a substitute for ASTM A240/A240M S31726 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A240/A240M S31726
0 active listings and RFQs →
ASTM A959 317LM
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S31726 and ASTM A959 317LM?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S31726 be substituted with ASTM A959 317LM?
ASTM A240/A240M S31726 and ASTM A959 317LM overlap closely enough on chemistry and mechanical properties that ASTM A959 317LM is often considered as a substitute for ASTM A240/A240M S31726 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.