ASTM A240/A240M S32506 vs EN 10088-1 X2CrNiMoCuWN25-7-4

Close Alternative — 76.7% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S32506 (ASTM A240/A240M:2025) and EN 10088-1 X2CrNiMoCuWN25-7-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S32506 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A240/A240M S32506 vs EN 10088-1 X2CrNiMoCuWN25-7-4 is a 76.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.7%.

Frequently Compared With ASTM A240/A240M S32506:
EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
76.7%
MECHANICAL MATCH
No shared data
OVERALL
76.7%
Specifications
Property ASTM A240/A240M S32506 EN 10088-1 X2CrNiMoCuWN25-7-4
Standard ASTM A240/A240M:2025 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.035
S (%) <=0.015 <=0.015
Si (%) <=0.90 <=1.00
Cr (%) 24.0-26.0 24.0-26.0
Ni (%) 5.5-7.2 6.0-8.0
Mo (%) 3.0-3.5 3.0-4.0
N (%) 0.08-0.20 0.20-0.30
W (%) 0.05-0.30 0.50-1.00
Cu (%) Not specified 0.50-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S32506 EN 10088-1 X2CrNiMoCuWN25-7-4
Tensile Strength >=620 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=18% Not specified
Hardness <=302 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S32506
Pressure vessels and general applications (plate, sheet and strip)
EN 10088-1 X2CrNiMoCuWN25-7-4
Not documented
Key Differences
Can ASTM A240/A240M S32506 Be Substituted With EN 10088-1 X2CrNiMoCuWN25-7-4?
ASTM A240/A240M S32506 and EN 10088-1 X2CrNiMoCuWN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S32506
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuWN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S32506 and EN 10088-1 X2CrNiMoCuWN25-7-4?
EN 10088-1 X2CrNiMoCuWN25-7-4 specifies Cu which is not specified for ASTM A240/A240M S32506.
Can ASTM A240/A240M S32506 be substituted with EN 10088-1 X2CrNiMoCuWN25-7-4?
ASTM A240/A240M S32506 and EN 10088-1 X2CrNiMoCuWN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.