ASTM A240/A240M S34565 vs EN 10088-3 X2CrNiMnMoN25-18-6-5

Related Material — 69.1% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S34565 (ASTM A240/A240M:2025) and EN 10088-3 X2CrNiMnMoN25-18-6-5 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S34565 is typically used for pressure vessels and general applications (plate, sheet and strip), while EN 10088-3 X2CrNiMnMoN25-18-6-5 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. ASTM A240/A240M S34565 is defined under ASTM International, originating from United States, while EN 10088-3 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A240/A240M S34565 vs EN 10088-3 X2CrNiMnMoN25-18-6-5 is a 87% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a related material overall at 69.1%.

Frequently Compared With ASTM A240/A240M S34565:
GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
87%
MECHANICAL MATCH
33.3%
OVERALL
69.1%
Specifications
Property ASTM A240/A240M S34565 EN 10088-3 X2CrNiMnMoN25-18-6-5
Standard ASTM A240/A240M:2025 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 5.00-7.00 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 23.0-25.0 24.0-26.0
Ni (%) 16.0-18.0 16.0-19.0
Mo (%) 4.0-5.0 4.0-5.0
N (%) 0.40-0.60 0.30-0.60
Nb (%) <=0.10 <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S34565 EN 10088-3 X2CrNiMnMoN25-18-6-5
Tensile Strength >=795 MPa 800-950 MPa
Yield Strength >=415 MPa >=420 MPa
Elongation >=35% >=35%
Hardness <=241 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
ASTM A240/A240M S34565
Pressure vessels and general applications (plate, sheet and strip)
EN 10088-3 X2CrNiMnMoN25-18-6-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can ASTM A240/A240M S34565 Be Substituted With EN 10088-3 X2CrNiMnMoN25-18-6-5?
ASTM A240/A240M S34565 and EN 10088-3 X2CrNiMnMoN25-18-6-5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A240/A240M S34565
0 active listings and RFQs →
EN 10088-3 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S34565 and EN 10088-3 X2CrNiMnMoN25-18-6-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S34565 be substituted with EN 10088-3 X2CrNiMnMoN25-18-6-5?
ASTM A240/A240M S34565 and EN 10088-3 X2CrNiMnMoN25-18-6-5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.