ASTM A240/A240M S35140 vs ASTM A959 S20162

Related Material — 58% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S35140 (ASTM A240/A240M:2025) and ASTM A959 S20162 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S35140 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S20162 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S35140 is defined under ASTM International, originating from United States, while ASTM A959 S20162 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S35140 vs ASTM A959 S20162 is a 58% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 58%.

Frequently Compared With ASTM A240/A240M S35140:
IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
58%
MECHANICAL MATCH
No shared data
OVERALL
58%
Specifications
Property ASTM A240/A240M S35140 ASTM A959 S20162
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.15
Mn (%) 1.00-3.00 4.0-8.0
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.040
Si (%) <=0.75 2.5-4.5
Cr (%) 20.0-22.0 16.5-21.0
Ni (%) 25.0-27.0 6.0-10.0
Mo (%) 1.00-2.00 0.50-2.50
N (%) 0.08-0.20 0.05-0.25
Nb (%) 0.25-0.75 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S35140 ASTM A959 S20162
Tensile Strength >=620 MPa Not specified
Yield Strength >=275 MPa Not specified
Elongation >=30% Not specified
Hardness <=241 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S35140
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S20162
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S35140 Be Substituted With ASTM A959 S20162?
ASTM A240/A240M S35140 and ASTM A959 S20162 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A240/A240M S35140
0 active listings and RFQs →
ASTM A959 S20162
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S35140 and ASTM A959 S20162?
ASTM A240/A240M S35140 specifies Nb which is not specified for ASTM A959 S20162.
Can ASTM A240/A240M S35140 be substituted with ASTM A959 S20162?
ASTM A240/A240M S35140 and ASTM A959 S20162 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.