ASTM A240/A240M S39274 vs ASTM A959 S32760

Close Alternative — 81.9% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S39274 (ASTM A240/A240M:2025) and ASTM A959 S32760 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S39274 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S32760 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S39274 is defined under ASTM International, originating from United States, while ASTM A959 S32760 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S39274 vs ASTM A959 S32760 is a 81.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.9%.

Frequently Compared With ASTM A240/A240M S39274:
EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
81.9%
MECHANICAL MATCH
No shared data
OVERALL
81.9%
Specifications
Property ASTM A240/A240M S39274 ASTM A959 S32760
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.030 <=0.030
S (%) <=0.020 <=0.010
Si (%) <=0.80 <=1.00
Cr (%) 24.0-26.0 24.0-26.0
Ni (%) 6.0-8.0 6.0-8.0
Mo (%) 2.5-3.5 3.0-4.0
N (%) 0.24-0.32 0.20-0.30
Cu (%) 0.20-0.80 0.50-1.00
W (%) 1.50-2.50 0.50-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S39274 ASTM A959 S32760
Tensile Strength >=800 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=15% Not specified
Hardness <=310 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S39274
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S32760
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A240/A240M S39274 Be Substituted With ASTM A959 S32760?
ASTM A240/A240M S39274 and ASTM A959 S32760 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S39274
0 active listings and RFQs →
ASTM A959 S32760
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S39274 and ASTM A959 S32760?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S39274 be substituted with ASTM A959 S32760?
ASTM A240/A240M S39274 and ASTM A959 S32760 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.