ASTM A240/A240M S40975 vs ASTM A959 S40945

Strong Match — 87.2% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S40975 (ASTM A240/A240M:2025) and ASTM A959 S40945 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S40975 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S40945 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S40975 is defined under ASTM International, originating from United States, while ASTM A959 S40945 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S40975 vs ASTM A959 S40945 is a 87.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.2%.

Frequently Compared With ASTM A240/A240M S40975:
ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
No shared data
OVERALL
87.2%
Specifications
Property ASTM A240/A240M S40975 ASTM A959 S40945
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 10.5-11.7 10.5-11.7
Ni (%) 0.50-1.00 <=0.50
N (%) <=0.030 <=0.030
Ti (%) <=0.75 0.05-0.20
Cb (%) Not specified 0.18-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S40975 ASTM A959 S40945
Tensile Strength >=415 MPa Not specified
Yield Strength >=275 MPa Not specified
Elongation >=20% Not specified
Hardness <=197 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S40975
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S40945
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S40975 Be Substituted With ASTM A959 S40945?
ASTM A240/A240M S40975 and ASTM A959 S40945 overlap closely enough on chemistry and mechanical properties that ASTM A959 S40945 is often considered as a substitute for ASTM A240/A240M S40975 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A240/A240M S40975
0 active listings and RFQs →
ASTM A959 S40945
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S40975 and ASTM A959 S40945?
ASTM A959 S40945 specifies Cb which is not specified for ASTM A240/A240M S40975.
Can ASTM A240/A240M S40975 be substituted with ASTM A959 S40945?
ASTM A240/A240M S40975 and ASTM A959 S40945 overlap closely enough on chemistry and mechanical properties that ASTM A959 S40945 is often considered as a substitute for ASTM A240/A240M S40975 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.