ASTM A240/A240M S43035 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S43035 (ASTM A240/A240M:2025) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S43035 is typically used for pressure vessels and general applications (plate, sheet and strip), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. ASTM A240/A240M S43035 is defined under ASTM International, originating from United States, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A240/A240M S43035 vs EN 10088-1 1.4006 is a 54.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A240/A240M S43035:
EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 201L
Match Breakdown
CHEMISTRY MATCH
54.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A240/A240M S43035 EN 10088-1 1.4006
Standard ASTM A240/A240M:2025 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08–0.15
Mn (%) <=1.00 ≤1.50
P (%) <=0.040 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.00
Cr (%) 17.0-19.0 11.5–13.5
Ni (%) <=0.50 ≤0.75
N (%) <=0.030 Not specified
Ti (%) <=1.10 Not specified
Al (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S43035 EN 10088-1 1.4006
Tensile Strength >=415 MPa ≥540 MPa (annealed)
Yield Strength >=205 MPa Not specified
Elongation >=22% ≥18%
Hardness <=183 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
ASTM A240/A240M S43035
Pressure vessels and general applications (plate, sheet and strip)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can ASTM A240/A240M S43035 Be Substituted With EN 10088-1 1.4006?
ASTM A240/A240M S43035 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A240/A240M S43035
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
ASTM A240/A240M S43035
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S43035 and EN 10088-1 1.4006?
ASTM A240/A240M S43035 specifies P, S, N, Ti which are not specified for EN 10088-1 1.4006.
Can ASTM A240/A240M S43035 be substituted with EN 10088-1 1.4006?
ASTM A240/A240M S43035 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.