ASTM A240/A240M S43932 vs ASTM A240/A240M S46800

Close Alternative — 79.3% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S43932 (ASTM A240/A240M:2025) and ASTM A240/A240M S46800 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S43932 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A240/A240M S46800 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A240/A240M S43932 is defined under ASTM International, originating from United States, while ASTM A240/A240M S46800 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S43932 vs ASTM A240/A240M S46800 is a 81.5% match. As per mechanical properties, the match is 75%. Combined, this makes them a close alternative overall at 79.3%.

Frequently Compared With ASTM A240/A240M S43932:
IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- ASTM A959 201L GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
81.5%
MECHANICAL MATCH
75%
OVERALL
79.3%
Specifications
Property ASTM A240/A240M S43932 ASTM A240/A240M S46800
Standard ASTM A240/A240M:2025 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 17.0-19.0 18.0-20.0
Ni (%) <=0.50 <=0.50
N (%) <=0.030 <=0.030
Al (%) <=0.15 Not specified
Ti (%) Not specified 0.07-0.30
Nb (%) Not specified 0.10-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S43932 ASTM A240/A240M S46800
Tensile Strength >=415 MPa >=415 MPa
Yield Strength >=205 MPa >=205 MPa
Elongation >=22% >=22%
Hardness <=183 HB <=90 HRBW
Condition Plate, sheet and strip; yield by 0.2 percent offset Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A240/A240M S43932
Pressure vessels and general applications (plate, sheet and strip)
ASTM A240/A240M S46800
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can ASTM A240/A240M S43932 Be Substituted With ASTM A240/A240M S46800?
ASTM A240/A240M S43932 and ASTM A240/A240M S46800 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S43932
0 active listings and RFQs →
ASTM A240/A240M S46800
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S43932 and ASTM A240/A240M S46800?
ASTM A240/A240M S43932 specifies Al which is not specified for ASTM A240/A240M S46800. ASTM A240/A240M S46800 specifies Ti, Nb which are not specified for ASTM A240/A240M S43932.
Can ASTM A240/A240M S43932 be substituted with ASTM A240/A240M S46800?
ASTM A240/A240M S43932 and ASTM A240/A240M S46800 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.