ASTM A240/A240M S43940 vs ASTM A959 S43940

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S43940 (ASTM A240/A240M:2025) and ASTM A959 S43940 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S43940 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S43940 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S43940 is defined under ASTM International, originating from United States, while ASTM A959 S43940 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S43940 vs ASTM A959 S43940 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A240/A240M S43940:
EN 10088-1 1.4845 GOST 5632 08X18H10 ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A240/A240M S43940 ASTM A959 S43940
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 17.5-18.5 17.5-18.5
Ti (%) 0.10-0.60 0.10-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S43940 ASTM A959 S43940
Tensile Strength >=430 MPa Not specified
Yield Strength >=250 MPa Not specified
Elongation >=18% Not specified
Hardness <=180 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S43940
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S43940
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A240/A240M S43940 Be Substituted With ASTM A959 S43940?
ASTM A240/A240M S43940 and ASTM A959 S43940 overlap closely enough on chemistry and mechanical properties that ASTM A959 S43940 is often considered as a substitute for ASTM A240/A240M S43940 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A240/A240M S43940
0 active listings and RFQs →
ASTM A959 S43940
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S43940 and ASTM A959 S43940?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S43940 be substituted with ASTM A959 S43940?
ASTM A240/A240M S43940 and ASTM A959 S43940 overlap closely enough on chemistry and mechanical properties that ASTM A959 S43940 is often considered as a substitute for ASTM A240/A240M S43940 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.