ASTM A240/A240M S82441 vs EN 10088-3 X2CrNiMnMoCuN24-4-3-2

Close Alternative — 83.3% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S82441 (ASTM A240/A240M:2025) and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S82441 is typically used for pressure vessels and general applications (plate, sheet and strip), while EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. ASTM A240/A240M S82441 is defined under ASTM International, originating from United States, while EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A240/A240M S82441 vs EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is a 100% match. As per mechanical properties, the match is 50%. Combined, this makes them a close alternative overall at 83.3%.

Frequently Compared With ASTM A240/A240M S82441:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
50%
OVERALL
83.3%
Specifications
Property ASTM A240/A240M S82441 EN 10088-3 X2CrNiMnMoCuN24-4-3-2
Standard ASTM A240/A240M:2025 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 2.50-4.00 2.50-4.0
P (%) <=0.035 <=0.035
S (%) <=0.005 <=0.005
Si (%) <=0.70 <=0.70
Cr (%) 23.0-25.0 23.0-25.0
Ni (%) 3.0-4.5 3.0-4.5
Mo (%) 1.00-2.00 1.00-2.00
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.10-0.80 0.10-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S82441 EN 10088-3 X2CrNiMnMoCuN24-4-3-2
Tensile Strength >=740 MPa 650-900 MPa
Yield Strength >=540 MPa >=450 MPa
Elongation >=25% >=25%
Hardness <=290 HB <=290 HB
Condition t < 0.4 in. [10.0 mm] (first condition printed); yield by 0.2 percent offset Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
ASTM A240/A240M S82441
Pressure vessels and general applications (plate, sheet and strip)
EN 10088-3 X2CrNiMnMoCuN24-4-3-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can ASTM A240/A240M S82441 Be Substituted With EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
ASTM A240/A240M S82441 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S82441
0 active listings and RFQs →
EN 10088-3 X2CrNiMnMoCuN24-4-3-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S82441 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S82441 be substituted with EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
ASTM A240/A240M S82441 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.