ASTM A276/A276M N08020 vs EN 10088-1 1.4006

Minimal Match — 31.2% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08020 (ASTM A276/A276M:2017) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08020 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. ASTM A276/A276M N08020 is defined under ASTM International, originating from United States, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M N08020 vs EN 10088-1 1.4006 is a 46.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 31.2%.

Frequently Compared With ASTM A276/A276M N08020:
EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
46.8%
MECHANICAL MATCH
0%
OVERALL
31.2%
Specifications
Property ASTM A276/A276M N08020 EN 10088-1 1.4006
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.07 0.08–0.15
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.035 Not specified
Si (%) <=1.00 ≤1.00
Cr (%) 19.0-21.0 11.5–13.5
Ni (%) 32.0-38.0 ≤0.75
Mo (%) 2.00-3.00 Not specified
Cu (%) 3.0-4.0 Not specified
Nb (%) <=1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08020 EN 10088-1 1.4006
Tensile Strength >=550 MPa ≥540 MPa (annealed)
Yield Strength >=240 MPa Not specified
Elongation >=30% ≥18%
Condition Condition SA (Stabilized annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
ASTM A276/A276M N08020
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can ASTM A276/A276M N08020 Be Substituted With EN 10088-1 1.4006?
ASTM A276/A276M N08020 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M N08020
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
ASTM A276/A276M N08020
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08020 and EN 10088-1 1.4006?
ASTM A276/A276M N08020 specifies P, S, Mo, Cu which are not specified for EN 10088-1 1.4006.
Can ASTM A276/A276M N08020 be substituted with EN 10088-1 1.4006?
ASTM A276/A276M N08020 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.