ASTM A276/A276M N08367 vs ASTM A959 N08926

Close Alternative — 79% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08367 (ASTM A276/A276M:2017) and ASTM A959 N08926 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08367 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 N08926 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M N08367 is defined under ASTM International, originating from United States, while ASTM A959 N08926 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M N08367 vs ASTM A959 N08926 is a 79% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79%.

Frequently Compared With ASTM A276/A276M N08367:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
79%
MECHANICAL MATCH
No shared data
OVERALL
79%
Specifications
Property ASTM A276/A276M N08367 ASTM A959 N08926
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Mn (%) <=2.00 <=2.00
P (%) <=0.040 <=0.030
S (%) <=0.030 <=0.010
Si (%) <=1.00 <=0.50
Cr (%) 20.0-22.0 19.0-21.0
Ni (%) 23.5-25.5 24.0-26.0
Mo (%) 6.0-7.0 6.0-7.0
N (%) 0.18-0.25 0.15-0.25
Cu (%) <=0.75 0.50-1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08367 ASTM A959 N08926
Tensile Strength >=655 MPa Not specified
Yield Strength >=310 MPa Not specified
Elongation >=30% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M N08367
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 N08926
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M N08367 Be Substituted With ASTM A959 N08926?
ASTM A276/A276M N08367 and ASTM A959 N08926 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M N08367
0 active listings and RFQs →
ASTM A959 N08926
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08367 and ASTM A959 N08926?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M N08367 be substituted with ASTM A959 N08926?
ASTM A276/A276M N08367 and ASTM A959 N08926 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.