ASTM A276/A276M N08700 vs EN 10088-1 X2CrTi21

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08700 (ASTM A276/A276M:2017) and EN 10088-1 X2CrTi21 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08700 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrTi21 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M N08700 vs EN 10088-1 X2CrTi21 is a 69.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M N08700:
EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
69.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M N08700 EN 10088-1 X2CrTi21
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Mn (%) <=2.00 <=1.00
P (%) <=0.040 <=0.050
S (%) <=0.030 <=0.050
Si (%) <=1.00 <=1.00
Cr (%) 19.0-23.0 19.0-22.0
Ni (%) 24.0-26.0 <=0.50
Mo (%) 4.3-5.0 <=0.50
Cu (%) <=0.50 <=0.50
Nb (%) <=0.40 Not specified
Al (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08700 EN 10088-1 X2CrTi21
Tensile Strength >=550 MPa Not specified
Yield Strength >=240 MPa Not specified
Elongation >=30% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M N08700
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrTi21
Not documented
Key Differences
Can ASTM A276/A276M N08700 Be Substituted With EN 10088-1 X2CrTi21?
ASTM A276/A276M N08700 and EN 10088-1 X2CrTi21 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M N08700
0 active listings and RFQs →
EN 10088-1 X2CrTi21
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08700 and EN 10088-1 X2CrTi21?
ASTM A276/A276M N08700 specifies Nb which is not specified for EN 10088-1 X2CrTi21. EN 10088-1 X2CrTi21 specifies Al which is not specified for ASTM A276/A276M N08700.
Can ASTM A276/A276M N08700 be substituted with EN 10088-1 X2CrTi21?
ASTM A276/A276M N08700 and EN 10088-1 X2CrTi21 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.