Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M N08800 (ASTM A276/A276M:2017) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M N08800 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware.
ASTM A276/A276M N08800 is defined under ASTM International, originating from United States, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.
As per chemical composition, ASTM A276/A276M N08800 vs EN 10088-1 1.4301 is a 56.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M N08800
EN 10088-1 1.4301
Tensile Strength
>=515 MPa
≥520 MPa
Yield Strength
>=205 MPa
≥210 MPa
Elongation
>=30%
≥45%
Hardness
<=192 HB
≤215 HB
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Not specified
Typical Applications
ASTM A276/A276M N08800
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
ASTM A276/A276M N08800 specifies Fe, Cu, Al, Ti which are not specified for EN 10088-1 1.4301.
Can ASTM A276/A276M N08800 Be Substituted With EN 10088-1 1.4301?
ASTM A276/A276M N08800 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M N08800 and EN 10088-1 1.4301?
ASTM A276/A276M N08800 specifies Fe, Cu, Al, Ti which are not specified for EN 10088-1 1.4301.
Can ASTM A276/A276M N08800 be substituted with EN 10088-1 1.4301?
ASTM A276/A276M N08800 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.