ASTM A276/A276M N08810 vs ASTM A276/A276M N08811

Strong Match — 97.7% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08810 (ASTM A276/A276M:2017) and ASTM A276/A276M N08811 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08810 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A276/A276M N08811 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A276/A276M N08810 is defined under ASTM International, originating from United States, while ASTM A276/A276M N08811 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M N08810 vs ASTM A276/A276M N08811 is a 96.5% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97.7%.

Frequently Compared With ASTM A276/A276M N08810:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
96.5%
MECHANICAL MATCH
100%
OVERALL
97.7%
Specifications
Property ASTM A276/A276M N08810 ASTM A276/A276M N08811
Standard ASTM A276/A276M:2017 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) 0.05-0.10 0.06-0.10
Mn (%) <=1.50 <=1.50
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 19.0-23.0 19.0-23.0
Ni (%) 30.0-35.0 30.0-35.0
Fe (%) >=39.5 >=39.5
Cu (%) <=0.75 <=0.75
Al (%) 0.15-0.60 0.25-0.60
Ti (%) 0.15-0.60 0.25-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08810 ASTM A276/A276M N08811
Tensile Strength >=450 MPa >=450 MPa
Yield Strength >=170 MPa >=170 MPa
Elongation >=30% >=30%
Hardness <=192 HB <=192 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
ASTM A276/A276M N08810
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A276/A276M N08811
Stainless steel bars and shapes (hot-finished or cold-finished)
Can ASTM A276/A276M N08810 Be Substituted With ASTM A276/A276M N08811?
ASTM A276/A276M N08810 and ASTM A276/A276M N08811 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08811 is often considered as a substitute for ASTM A276/A276M N08810 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M N08810
0 active listings and RFQs →
ASTM A276/A276M N08811
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08810 and ASTM A276/A276M N08811?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M N08810 be substituted with ASTM A276/A276M N08811?
ASTM A276/A276M N08810 and ASTM A276/A276M N08811 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08811 is often considered as a substitute for ASTM A276/A276M N08810 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.