ASTM A276/A276M N08810 vs EN 10088-1 X10NiCrAlTi32-21

Strong Match — 88.6% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M N08810 (ASTM A276/A276M:2017) and EN 10088-1 X10NiCrAlTi32-21 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M N08810 is defined under ASTM International, originating from United States, while EN 10088-1 X10NiCrAlTi32-21 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M N08810 vs EN 10088-1 X10NiCrAlTi32-21 is a 88.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.6%.

Frequently Compared With ASTM A276/A276M N08810:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
88.6%
MECHANICAL MATCH
No shared data
OVERALL
88.6%
Specifications
Property ASTM A276/A276M N08810 EN 10088-1 X10NiCrAlTi32-21
Standard ASTM A276/A276M:2017 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.05-0.10 <=0.12
Mn (%) <=1.50 <=2.00
P (%) <=0.045 <=0.030
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 19.0-23.0 19.0-23.0
Ni (%) 30.0-35.0 30.0-34.0
Fe (%) >=39.5 Not specified
Cu (%) <=0.75 Not specified
Al (%) 0.15-0.60 0.15-0.60
Ti (%) 0.15-0.60 0.15-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M N08810 EN 10088-1 X10NiCrAlTi32-21
Tensile Strength >=450 MPa Not specified
Yield Strength >=170 MPa Not specified
Elongation >=30% Not specified
Hardness <=192 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M N08810
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X10NiCrAlTi32-21
Not documented
Key Differences
Can ASTM A276/A276M N08810 Be Substituted With EN 10088-1 X10NiCrAlTi32-21?
ASTM A276/A276M N08810 and EN 10088-1 X10NiCrAlTi32-21 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X10NiCrAlTi32-21 is often considered as a substitute for ASTM A276/A276M N08810 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M N08810
0 active listings and RFQs →
EN 10088-1 X10NiCrAlTi32-21
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M N08810 and EN 10088-1 X10NiCrAlTi32-21?
ASTM A276/A276M N08810 specifies Fe, Cu which are not specified for EN 10088-1 X10NiCrAlTi32-21.
Can ASTM A276/A276M N08810 be substituted with EN 10088-1 X10NiCrAlTi32-21?
ASTM A276/A276M N08810 and EN 10088-1 X10NiCrAlTi32-21 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X10NiCrAlTi32-21 is often considered as a substitute for ASTM A276/A276M N08810 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.