ASTM A276/A276M:2017 S20100 Steel: Specifications & Listings

ASTM A276/A276M:2017 S20100: S20100 (type 201): austenitic stainless steel bars and shapes. Specified in ASTM A276/A276M:2017.

Category: Stainless Steel
Grade Details
GradeASTM A276/A276M:2017 S20100
Standard ASTM A276/A276M:2017
ApplicationsStainless steel bars and shapes (hot-finished or cold-finished)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 1570 (Part 5) X10Cr17Mn6Ni4 IS 1570 (Part 5):1985 India No activity yet
ASTM A959 201 ASTM A959:2011 USA No activity yet
ASTM A240/A240M S20100 ASTM A240/A240M:2025 USA No activity yet
EN 10088-1 X12CrMnNiN17-7-5 EN 10088-1:2014 Europe (CEN) No activity yet
ASTM A959 202 ASTM A959:2011 USA No activity yet
ASTM A276/A276M S20200 ASTM A276/A276M:2017 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 201 ASTM A959:2011 Strong Match
EN 10088-1 X12CrMnNiN17-7-5 EN 10088-1:2014 Strong Match
EN 10088-1 X12CrMnNiN17-7-5 EN 10088-1:2023 Strong Match
IS 1570 (Part 5) X10Cr17Mn6Ni4 IS 1570 (Part 5):1985 Strong Match
ASTM A276/A276M S20200 ASTM A276/A276M:2017 Strong Match
ASTM A240/A240M S20100 ASTM A240/A240M:2025 Strong Match
ASTM A959 202 ASTM A959:2011 Strong Match
EN 10088-1 X12CrMnNiN18-9-5 EN 10088-1:2014 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn P S Si Cr Ni N
<=0.15 5.5-7.5 <=0.060 <=0.030 <=1.00 16.0-18.0 3.5-5.5 <=0.25
Mechanical Properties
Tensile Strength >=515 MPa
Yield Strength >=275 MPa
Elongation >=40%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)

More data from ASTM A276/A276M:2017

From the standard
Mechanical requirements by condition and size 1 row(s)
ConditionFinishDiameter or thickness, in. [mm]Tensile strength, min (MPa)Yield strength, min (MPa)Elongation, min (%)Reduction of area, min (%)Brinell HBW, max
A (Annealed)hot-finished or cold-finishedall5152754045-
Yield by the 0.2 percent offset method. Hardness is HBW unless otherwise indicated; equivalent Rockwell is permitted.
Source: ASTM A276/A276M:2017, Table 2

Active ASTM A276/A276M:2017 S20100 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active ASTM A276/A276M:2017 S20100 listings at this time.

Register for Alerts

Buyer RFQs for ASTM A276/A276M:2017 S20100

+ Post an RFQ for this grade

No open buyer requirements for ASTM A276/A276M:2017 S20100 at this time.

Register for Alerts