ASTM A276/A276M S20162 vs ASTM A959 XM-17

Related Material — 62.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S20162 (ASTM A276/A276M:2017) and ASTM A959 XM-17 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S20162 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 XM-17 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S20162 is defined under ASTM International, originating from United States, while ASTM A959 XM-17 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S20162 vs ASTM A959 XM-17 is a 62.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 62.9%.

Frequently Compared With ASTM A276/A276M S20162:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
62.9%
MECHANICAL MATCH
No shared data
OVERALL
62.9%
Specifications
Property ASTM A276/A276M S20162 ASTM A959 XM-17
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.08
Mn (%) 4.0-8.0 7.5-9.0
P (%) <=0.040 <=0.045
S (%) <=0.040 <=0.030
Si (%) 2.5-4.5 <=1.00
Cr (%) 16.5-21.0 17.5-20.5
Ni (%) 6.0-10.0 5.0-7.0
Mo (%) 0.50-2.50 2.00-3.00
N (%) 0.05-0.25 0.25-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S20162 ASTM A959 XM-17
Tensile Strength >=690 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=50% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S20162
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 XM-17
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S20162 Be Substituted With ASTM A959 XM-17?
ASTM A276/A276M S20162 and ASTM A959 XM-17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S20162
0 active listings and RFQs →
ASTM A959 XM-17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S20162 and ASTM A959 XM-17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S20162 be substituted with ASTM A959 XM-17?
ASTM A276/A276M S20162 and ASTM A959 XM-17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.