ASTM A276/A276M S20200 vs IS 1570 (Part 5) X10Cr17Mn6Ni4

Strong Match — 85.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S20200 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X10Cr17Mn6Ni4 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S20200 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X10Cr17Mn6Ni4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S20200 vs IS 1570 (Part 5) X10Cr17Mn6Ni4 is a 78.8% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 85.9%.

Frequently Compared With ASTM A276/A276M S20200:
ASTM A959 202 ASTM A959 201 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
78.8%
MECHANICAL MATCH
100%
OVERALL
85.9%
Specifications
Property ASTM A276/A276M S20200 IS 1570 (Part 5) X10Cr17Mn6Ni4
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.20
Mn (%) 7.5-10.0 4.0-8.0
P (%) <=0.060 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 17.0-19.0 16.0-18.0
Ni (%) 4.0-6.0 3.5-5.5
N (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S20200 IS 1570 (Part 5) X10Cr17Mn6Ni4
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=275 MPa >=275 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Annealed, quenched or solution treated bars and flats (Table 3)
Hardness Not specified <=217 HB
Typical Applications
ASTM A276/A276M S20200
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X10Cr17Mn6Ni4
Not documented
Key Differences
Can ASTM A276/A276M S20200 Be Substituted With IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A276/A276M S20200 and IS 1570 (Part 5) X10Cr17Mn6Ni4 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X10Cr17Mn6Ni4 is often considered as a substitute for ASTM A276/A276M S20200 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S20200
0 active listings and RFQs →
IS 1570 (Part 5) X10Cr17Mn6Ni4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S20200 and IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A276/A276M S20200 specifies N which is not specified for IS 1570 (Part 5) X10Cr17Mn6Ni4.
Can ASTM A276/A276M S20200 be substituted with IS 1570 (Part 5) X10Cr17Mn6Ni4?
ASTM A276/A276M S20200 and IS 1570 (Part 5) X10Cr17Mn6Ni4 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X10Cr17Mn6Ni4 is often considered as a substitute for ASTM A276/A276M S20200 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.