Minimal Match — 29.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S20910 (ASTM A276/A276M:2017) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S20910 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. ASTM A276/A276M S20910 is defined under ASTM International (United States).

As per chemical composition, ASTM A276/A276M S20910 vs GOST 5632 08X18H10 is a 44.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 29.8%.

Frequently Compared With ASTM A276/A276M S20910:
EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
44.7%
MECHANICAL MATCH
0%
OVERALL
29.8%
Specifications
Property ASTM A276/A276M S20910 GOST 5632 08X18H10
Standard ASTM A276/A276M:2017 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.06 ≤0.08
Mn (%) 4.0-6.0 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Si (%) <=1.00 ≤0.80
Cr (%) 20.5-23.5 17.0–19.0
Ni (%) 11.5-13.5 9.0–11.0
Mo (%) 1.50-3.00 Not specified
N (%) 0.20-0.40 Not specified
V (%) 0.10-0.30 Not specified
Nb (%) 0.10-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S20910 GOST 5632 08X18H10
Tensile Strength >=690 MPa ≥520 MPa
Yield Strength >=380 MPa ≥205 MPa
Elongation >=35% ≥40%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S20910
Stainless steel bars and shapes (hot-finished or cold-finished)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can ASTM A276/A276M S20910 Be Substituted With GOST 5632 08X18H10?
ASTM A276/A276M S20910 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S20910
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
ASTM A276/A276M S20910
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S20910 and GOST 5632 08X18H10?
ASTM A276/A276M S20910 specifies Mo, N, V, Nb which are not specified for GOST 5632 08X18H10.
Can ASTM A276/A276M S20910 be substituted with GOST 5632 08X18H10?
ASTM A276/A276M S20910 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.