ASTM A276/A276M S21800 vs IS 1570 (Part 5) X20Cr13

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S21800 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X20Cr13 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S21800 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X20Cr13 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S21800 vs IS 1570 (Part 5) X20Cr13 is a 57.4% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S21800:
ASTM A959 201 ASTM A959 202 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
57.4%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S21800 IS 1570 (Part 5) X20Cr13
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.10 0.16-0.25
Mn (%) 7.0-9.0 <=1.0
P (%) <=0.060 <=0.040
S (%) <=0.030 <=0.030
Si (%) 3.5-4.5 <=1.0
Cr (%) 16.0-18.0 12.0-14.0
Ni (%) 8.0-9.0 <=1.0
N (%) 0.08-0.18 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S21800 IS 1570 (Part 5) X20Cr13
Tensile Strength >=655 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=35% Not specified
Hardness <=241 HB <=241 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A276/A276M S21800
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X20Cr13
Not documented
Key Differences
Can ASTM A276/A276M S21800 Be Substituted With IS 1570 (Part 5) X20Cr13?
ASTM A276/A276M S21800 and IS 1570 (Part 5) X20Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S21800
0 active listings and RFQs →
IS 1570 (Part 5) X20Cr13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S21800 and IS 1570 (Part 5) X20Cr13?
ASTM A276/A276M S21800 specifies N which is not specified for IS 1570 (Part 5) X20Cr13.
Can ASTM A276/A276M S21800 be substituted with IS 1570 (Part 5) X20Cr13?
ASTM A276/A276M S21800 and IS 1570 (Part 5) X20Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.