ASTM A276/A276M S28200 vs EN 10088-1 1.4845

Minimal Match — 32.6% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S28200 (ASTM A276/A276M:2017) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S28200 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A276/A276M S28200 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S28200 vs EN 10088-1 1.4845 is a 48.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.6%.

Frequently Compared With ASTM A276/A276M S28200:
ASTM A959 .- IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
48.9%
MECHANICAL MATCH
0%
OVERALL
32.6%
Specifications
Property ASTM A276/A276M S28200 EN 10088-1 1.4845
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.15 ≤0.10
Mn (%) 17.0-19.0 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.50
Cr (%) 17.0-19.0 24.0–26.0
Mo (%) 0.75-1.25 Not specified
N (%) 0.40-0.60 Not specified
Cu (%) 0.75-1.25 Not specified
Ni (%) Not specified 19.0–22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S28200 EN 10088-1 1.4845
Tensile Strength >=760 MPa ≥515 MPa
Yield Strength >=410 MPa ≥205 MPa
Elongation >=35% ≥40%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A276/A276M S28200
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A276/A276M S28200 Be Substituted With EN 10088-1 1.4845?
ASTM A276/A276M S28200 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S28200
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A276/A276M S28200
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S28200 and EN 10088-1 1.4845?
ASTM A276/A276M S28200 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845. EN 10088-1 1.4845 specifies Ni which is not specified for ASTM A276/A276M S28200.
Can ASTM A276/A276M S28200 be substituted with EN 10088-1 1.4845?
ASTM A276/A276M S28200 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.