Strong Match — 98% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S30200 (ASTM A276/A276M:2017) and IS 5522 X07Cr18Ni9 (IS 5522:2014) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S30200 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 5522 X07Cr18Ni9 is commonly used for utensils.
ASTM A276/A276M S30200 is defined under ASTM International, originating from United States, while IS 5522 X07Cr18Ni9 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A276/A276M S30200 vs IS 5522 X07Cr18Ni9 is a 96.9% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 98%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S30200
IS 5522 X07Cr18Ni9
Tensile Strength
>=515 MPa
>=515 MPa
Yield Strength
>=205 MPa
>=205 MPa
Elongation
>=40%
>=40%
Condition
Condition A (Annealed), hot-finished, all sizes (first row printed)
Annealed/softened
Hardness
Not specified
<=201 HB
Typical Applications
ASTM A276/A276M S30200
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 5522 X07Cr18Ni9
Utensils
Can ASTM A276/A276M S30200 Be Substituted With IS 5522 X07Cr18Ni9?
ASTM A276/A276M S30200 and IS 5522 X07Cr18Ni9 overlap closely enough on chemistry and mechanical properties that IS 5522 X07Cr18Ni9 is often considered as a substitute for ASTM A276/A276M S30200 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A276/A276M S30200 and IS 5522 X07Cr18Ni9?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S30200 be substituted with IS 5522 X07Cr18Ni9?
ASTM A276/A276M S30200 and IS 5522 X07Cr18Ni9 overlap closely enough on chemistry and mechanical properties that IS 5522 X07Cr18Ni9 is often considered as a substitute for ASTM A276/A276M S30200 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.