ASTM A276/A276M S30403 vs EN 10088-1 1.4845

Related Material — 56.4% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S30403 (ASTM A276/A276M:2017) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S30403 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A276/A276M S30403 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S30403 vs EN 10088-1 1.4845 is a 67.9% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a related material overall at 56.4%.

Frequently Compared With ASTM A276/A276M S30403:
EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
67.9%
MECHANICAL MATCH
33.3%
OVERALL
56.4%
Specifications
Property ASTM A276/A276M S30403 EN 10088-1 1.4845
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.10
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.50
Cr (%) 18.0-20.0 24.0–26.0
Ni (%) 8.0-12.0 19.0–22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S30403 EN 10088-1 1.4845
Tensile Strength >=485 MPa ≥515 MPa
Yield Strength >=170 MPa ≥205 MPa
Elongation >=40% ≥40%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A276/A276M S30403
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A276/A276M S30403 Be Substituted With EN 10088-1 1.4845?
ASTM A276/A276M S30403 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S30403
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A276/A276M S30403
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S30403 and EN 10088-1 1.4845?
ASTM A276/A276M S30403 specifies P, S which are not specified for EN 10088-1 1.4845.
Can ASTM A276/A276M S30403 be substituted with EN 10088-1 1.4845?
ASTM A276/A276M S30403 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.