ASTM A276/A276M S30453 vs EN 10088-1 1.4845

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S30453 (ASTM A276/A276M:2017) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S30453 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A276/A276M S30453 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S30453 vs EN 10088-1 1.4845 is a 62.4% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S30453:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
62.4%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S30453 EN 10088-1 1.4845
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.10
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.50
Cr (%) 18.0-20.0 24.0–26.0
Ni (%) 8.0-11.0 19.0–22.0
N (%) 0.10-0.16 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S30453 EN 10088-1 1.4845
Tensile Strength >=515 MPa ≥515 MPa
Yield Strength >=205 MPa ≥205 MPa
Elongation >=40% ≥40%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A276/A276M S30453
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A276/A276M S30453 Be Substituted With EN 10088-1 1.4845?
ASTM A276/A276M S30453 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S30453
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A276/A276M S30453
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S30453 and EN 10088-1 1.4845?
ASTM A276/A276M S30453 specifies P, S, N which are not specified for EN 10088-1 1.4845.
Can ASTM A276/A276M S30453 be substituted with EN 10088-1 1.4845?
ASTM A276/A276M S30453 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.