ASTM A276/A276M S30454 vs EN 10088-1 1.4301

Minimal Match — 49.5% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S30454 (ASTM A276/A276M:2017) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S30454 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. ASTM A276/A276M S30454 is defined under ASTM International, originating from United States, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S30454 vs EN 10088-1 1.4301 is a 74.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 49.5%.

Frequently Compared With ASTM A276/A276M S30454:
IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
74.3%
MECHANICAL MATCH
0%
OVERALL
49.5%
Specifications
Property ASTM A276/A276M S30454 EN 10088-1 1.4301
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.03 ≤0.07
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 ≤0.045
S (%) <=0.030 ≤0.030
Si (%) <=1.00 ≤1.00
Cr (%) 18.0-20.0 17.5–19.5
Ni (%) 8.0-11.0 8.0–10.5
N (%) 0.16-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S30454 EN 10088-1 1.4301
Tensile Strength >=620 MPa ≥520 MPa
Yield Strength >=345 MPa ≥210 MPa
Elongation >=30% ≥45%
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Hardness Not specified ≤215 HB
Typical Applications
ASTM A276/A276M S30454
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can ASTM A276/A276M S30454 Be Substituted With EN 10088-1 1.4301?
ASTM A276/A276M S30454 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S30454
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
ASTM A276/A276M S30454
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S30454 and EN 10088-1 1.4301?
ASTM A276/A276M S30454 specifies N which is not specified for EN 10088-1 1.4301.
Can ASTM A276/A276M S30454 be substituted with EN 10088-1 1.4301?
ASTM A276/A276M S30454 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.