ASTM A276/A276M S30800 vs ASTM A276/A276M S32100

Strong Match — 89.2% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S30800 (ASTM A276/A276M:2017) and ASTM A276/A276M S32100 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S30800 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A276/A276M S32100 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). ASTM A276/A276M S30800 is defined under ASTM International, originating from United States, while ASTM A276/A276M S32100 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S30800 vs ASTM A276/A276M S32100 is a 83.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 89.2%.

Frequently Compared With ASTM A276/A276M S30800:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
83.7%
MECHANICAL MATCH
100%
OVERALL
89.2%
Specifications
Property ASTM A276/A276M S30800 ASTM A276/A276M S32100
Standard ASTM A276/A276M:2017 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cr (%) 19.0-21.0 17.0-19.0
Ni (%) 10.0-12.0 9.0-12.0
Ti (%) Not specified <=0.70
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S30800 ASTM A276/A276M S32100
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa
Elongation >=40% >=40%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
ASTM A276/A276M S30800
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A276/A276M S32100
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can ASTM A276/A276M S30800 Be Substituted With ASTM A276/A276M S32100?
ASTM A276/A276M S30800 and ASTM A276/A276M S32100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32100 is often considered as a substitute for ASTM A276/A276M S30800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S30800
0 active listings and RFQs →
ASTM A276/A276M S32100
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S30800 and ASTM A276/A276M S32100?
ASTM A276/A276M S32100 specifies Ti which is not specified for ASTM A276/A276M S30800.
Can ASTM A276/A276M S30800 be substituted with ASTM A276/A276M S32100?
ASTM A276/A276M S30800 and ASTM A276/A276M S32100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32100 is often considered as a substitute for ASTM A276/A276M S30800 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.