ASTM A276/A276M S31010 vs ASTM A959 S32906

Related Material — 62.5% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31010 (ASTM A276/A276M:2017) and ASTM A959 S32906 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31010 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S32906 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S31010 is defined under ASTM International, originating from United States, while ASTM A959 S32906 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S31010 vs ASTM A959 S32906 is a 62.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 62.5%.

Frequently Compared With ASTM A276/A276M S31010:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
62.5%
MECHANICAL MATCH
No shared data
OVERALL
62.5%
Specifications
Property ASTM A276/A276M S31010 ASTM A959 S32906
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 5.50-6.50 0.80-1.50
P (%) <=0.030 <=0.030
S (%) <=0.0010 <=0.030
Si (%) 0.25-0.75 <=0.50
Cr (%) 28.5-30.5 28.0-30.0
Ni (%) 14.0-16.0 5.8-7.5
Mo (%) 1.5-2.5 1.50-2.60
N (%) 0.80-0.90 0.30-0.40
Al (%) <=0.05 Not specified
B (%) <=0.005 Not specified
Cu (%) Not specified <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31010 ASTM A959 S32906
Tensile Strength >=760 MPa Not specified
Yield Strength >=515 MPa Not specified
Elongation >=40% Not specified
Hardness <=330 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S31010
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S32906
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A276/A276M S31010 Be Substituted With ASTM A959 S32906?
ASTM A276/A276M S31010 and ASTM A959 S32906 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S31010
0 active listings and RFQs →
ASTM A959 S32906
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31010 and ASTM A959 S32906?
ASTM A276/A276M S31010 specifies Al, B which are not specified for ASTM A959 S32906. ASTM A959 S32906 specifies Cu which is not specified for ASTM A276/A276M S31010.
Can ASTM A276/A276M S31010 be substituted with ASTM A959 S32906?
ASTM A276/A276M S31010 and ASTM A959 S32906 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.