ASTM A276/A276M S31010 vs EN 10088-1 X3CrNiMoBN17-13-3

Related Material — 58.1% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31010 (ASTM A276/A276M:2017) and EN 10088-1 X3CrNiMoBN17-13-3 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31010 is defined under ASTM International, originating from United States, while EN 10088-1 X3CrNiMoBN17-13-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S31010 vs EN 10088-1 X3CrNiMoBN17-13-3 is a 58.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 58.1%.

Frequently Compared With ASTM A276/A276M S31010:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
58.1%
MECHANICAL MATCH
No shared data
OVERALL
58.1%
Specifications
Property ASTM A276/A276M S31010 EN 10088-1 X3CrNiMoBN17-13-3
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.04
Mn (%) 5.50-6.50 <=2.00
P (%) <=0.030 <=0.035
S (%) <=0.0010 <=0.015
Si (%) 0.25-0.75 <=0.75
Cr (%) 28.5-30.5 16.0-18.0
Ni (%) 14.0-16.0 12.0-14.0
Mo (%) 1.5-2.5 2.00-3.00
N (%) 0.80-0.90 0.10-0.18
Al (%) <=0.05 Not specified
B (%) <=0.005 0.0015-0.0050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31010 EN 10088-1 X3CrNiMoBN17-13-3
Tensile Strength >=760 MPa Not specified
Yield Strength >=515 MPa Not specified
Elongation >=40% Not specified
Hardness <=330 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S31010
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X3CrNiMoBN17-13-3
Not documented
Key Differences
Can ASTM A276/A276M S31010 Be Substituted With EN 10088-1 X3CrNiMoBN17-13-3?
ASTM A276/A276M S31010 and EN 10088-1 X3CrNiMoBN17-13-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S31010
0 active listings and RFQs →
EN 10088-1 X3CrNiMoBN17-13-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31010 and EN 10088-1 X3CrNiMoBN17-13-3?
ASTM A276/A276M S31010 specifies Al which is not specified for EN 10088-1 X3CrNiMoBN17-13-3.
Can ASTM A276/A276M S31010 be substituted with EN 10088-1 X3CrNiMoBN17-13-3?
ASTM A276/A276M S31010 and EN 10088-1 X3CrNiMoBN17-13-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.