ASTM A276/A276M S31100 vs EN 10088-1 X5CrNi18-10

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31100 (ASTM A276/A276M:2017) and EN 10088-1 X5CrNi18-10 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31100 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 X5CrNi18-10 is commonly used for food, chemical, architectural applications. ASTM A276/A276M S31100 is defined under ASTM International, originating from United States, while EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S31100 vs EN 10088-1 X5CrNi18-10 is a 70.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S31100:
IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.8%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S31100 EN 10088-1 X5CrNi18-10
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.07
Mn (%) <=1.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 25.0-27.0 17.5-19.5
Ni (%) 6.0-7.0 8.0-10.5
Ti (%) <=0.25 Not specified
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31100 EN 10088-1 X5CrNi18-10
Tensile Strength >=620 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=20% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S31100
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X5CrNi18-10
Food, chemical, architectural applications
Key Differences
Can ASTM A276/A276M S31100 Be Substituted With EN 10088-1 X5CrNi18-10?
ASTM A276/A276M S31100 and EN 10088-1 X5CrNi18-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S31100
No active listings currently.
EN 10088-1 X5CrNi18-10
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3900 mm (98.43–153.54 in)
On M-EX Right Now
ASTM A276/A276M S31100
0 active listings and RFQs →
EN 10088-1 X5CrNi18-10
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31100 and EN 10088-1 X5CrNi18-10?
ASTM A276/A276M S31100 specifies Ti which is not specified for EN 10088-1 X5CrNi18-10. EN 10088-1 X5CrNi18-10 specifies N which is not specified for ASTM A276/A276M S31100.
Can ASTM A276/A276M S31100 be substituted with EN 10088-1 X5CrNi18-10?
ASTM A276/A276M S31100 and EN 10088-1 X5CrNi18-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.