ASTM A276/A276M S31100 vs IS 1570 (Part 5) X30Cr13

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31100 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X30Cr13 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31100 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X30Cr13 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S31100 vs IS 1570 (Part 5) X30Cr13 is a 70.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A276/A276M S31100:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A276/A276M S31100 IS 1570 (Part 5) X30Cr13
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.06 0.26-0.35
Mn (%) <=1.00 <=1.0
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 25.0-27.0 12.0-14.0
Ni (%) 6.0-7.0 <=1.0
Ti (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31100 IS 1570 (Part 5) X30Cr13
Tensile Strength >=620 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=20% Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=241 HB
Typical Applications
ASTM A276/A276M S31100
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X30Cr13
Not documented
Key Differences
Can ASTM A276/A276M S31100 Be Substituted With IS 1570 (Part 5) X30Cr13?
ASTM A276/A276M S31100 and IS 1570 (Part 5) X30Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S31100
0 active listings and RFQs →
IS 1570 (Part 5) X30Cr13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31100 and IS 1570 (Part 5) X30Cr13?
ASTM A276/A276M S31100 specifies Ti which is not specified for IS 1570 (Part 5) X30Cr13.
Can ASTM A276/A276M S31100 be substituted with IS 1570 (Part 5) X30Cr13?
ASTM A276/A276M S31100 and IS 1570 (Part 5) X30Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.