ASTM A276/A276M S31266 vs IS 6603 X01Cr24Ni22Mo4CuNW
Related Material — 67.1% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S31266 (ASTM A276/A276M:2017) and IS 6603 X01Cr24Ni22Mo4CuNW (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S31266 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 6603 X01Cr24Ni22Mo4CuNW is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
ASTM A276/A276M S31266 is defined under ASTM International, originating from United States, while IS 6603 X01Cr24Ni22Mo4CuNW is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, ASTM A276/A276M S31266 vs IS 6603 X01Cr24Ni22Mo4CuNW is a 84% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a related material overall at 67.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S31266
IS 6603 X01Cr24Ni22Mo4CuNW
Tensile Strength
>=750 MPa
800-1000 MPa
Yield Strength
>=420 MPa
>=420 MPa
Elongation
>=35%
>=50%
Condition
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 60 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
ASTM A276/A276M S31266
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 6603 X01Cr24Ni22Mo4CuNW
General purposes, semi-finished products, bars, wire rods and bright bars
Can ASTM A276/A276M S31266 Be Substituted With IS 6603 X01Cr24Ni22Mo4CuNW?
ASTM A276/A276M S31266 and IS 6603 X01Cr24Ni22Mo4CuNW share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between ASTM A276/A276M S31266 and IS 6603 X01Cr24Ni22Mo4CuNW?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S31266 be substituted with IS 6603 X01Cr24Ni22Mo4CuNW?
ASTM A276/A276M S31266 and IS 6603 X01Cr24Ni22Mo4CuNW share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.