Strong Match — 90.4% match
based on chemical composition and mechanical property overlap.
ASTM A276/A276M S31603 (ASTM A276/A276M:2017) and BS 970 (Part 3) 316S11 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Stainless Steel category.
ASTM A276/A276M S31603 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while BS 970 (Part 3) 316S11 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (table 18).
ASTM A276/A276M S31603 is defined under ASTM International, originating from United States, while BS 970 (Part 3) 316S11 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, ASTM A276/A276M S31603 vs BS 970 (Part 3) 316S11 is a 90.4% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 90.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
ASTM A276/A276M S31603
BS 970 (Part 3) 316S11
Tensile Strength
>=485 MPa
Not specified
Yield Strength
>=170 MPa
Not specified
Elongation
>=40%
Not specified
Condition
Condition A (Annealed), hot-finished, all sizes (first row printed)
Not specified
Typical Applications
ASTM A276/A276M S31603
Stainless steel bars and shapes (hot-finished or cold-finished)
BS 970 (Part 3) 316S11
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (Table 18)
Can ASTM A276/A276M S31603 Be Substituted With BS 970 (Part 3) 316S11?
ASTM A276/A276M S31603 and BS 970 (Part 3) 316S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S11 is often considered as a substitute for ASTM A276/A276M S31603 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between ASTM A276/A276M S31603 and BS 970 (Part 3) 316S11?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S31603 be substituted with BS 970 (Part 3) 316S11?
ASTM A276/A276M S31603 and BS 970 (Part 3) 316S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S11 is often considered as a substitute for ASTM A276/A276M S31603 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.