ASTM A276/A276M S31640 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 30.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31640 (ASTM A276/A276M:2017) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31640 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. ASTM A276/A276M S31640 is defined under ASTM International, originating from United States, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S31640 vs IS 1570 (Part 7) 12Cr12MoVH is a 46.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 30.8%.

Frequently Compared With ASTM A276/A276M S31640:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
46.2%
MECHANICAL MATCH
0%
OVERALL
30.8%
Specifications
Property ASTM A276/A276M S31640 IS 1570 (Part 7) 12Cr12MoVH
Standard ASTM A276/A276M:2017 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08-0.16
Mn (%) <=2.00 0.40-1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.035
Si (%) <=1.00 <=0.60
Cr (%) 16.0-18.0 11.5-13.00
Ni (%) 10.0-14.0 <=1.0
Mo (%) 2.00-3.00 0.40-0.80
N (%) <=0.10 Not specified
Nb (%) <=1.10 Not specified
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31640 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength >=515 MPa 770-930 MPa
Yield Strength >=205 MPa >=585 MPa (0.2 % proof stress)
Elongation >=40% >=15%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
ASTM A276/A276M S31640
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can ASTM A276/A276M S31640 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
ASTM A276/A276M S31640 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A276/A276M S31640
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31640 and IS 1570 (Part 7) 12Cr12MoVH?
ASTM A276/A276M S31640 specifies N, Nb which are not specified for IS 1570 (Part 7) 12Cr12MoVH. IS 1570 (Part 7) 12Cr12MoVH specifies V which is not specified for ASTM A276/A276M S31640.
Can ASTM A276/A276M S31640 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
ASTM A276/A276M S31640 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.