ASTM A276/A276M S31653 vs EN 10088-1 X2CrNiMoN17-11-2

Strong Match — 86% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31653 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiMoN17-11-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31653 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMoN17-11-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S31653 vs EN 10088-1 X2CrNiMoN17-11-2 is a 86% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86%.

Frequently Compared With ASTM A276/A276M S31653:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
86%
MECHANICAL MATCH
No shared data
OVERALL
86%
Specifications
Property ASTM A276/A276M S31653 EN 10088-1 X2CrNiMoN17-11-2
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 16.0-18.0 16.5-18.5
Ni (%) 10.0-13.0 10.0-12.5
Mo (%) 2.00-3.00 2.00-2.50
N (%) 0.10-0.16 0.12-0.22
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31653 EN 10088-1 X2CrNiMoN17-11-2
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=40% Not specified
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S31653
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiMoN17-11-2
Not documented
Can ASTM A276/A276M S31653 Be Substituted With EN 10088-1 X2CrNiMoN17-11-2?
ASTM A276/A276M S31653 and EN 10088-1 X2CrNiMoN17-11-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN17-11-2 is often considered as a substitute for ASTM A276/A276M S31653 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S31653
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN17-11-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31653 and EN 10088-1 X2CrNiMoN17-11-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S31653 be substituted with EN 10088-1 X2CrNiMoN17-11-2?
ASTM A276/A276M S31653 and EN 10088-1 X2CrNiMoN17-11-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN17-11-2 is often considered as a substitute for ASTM A276/A276M S31653 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.