ASTM A276/A276M S31700 vs IS 1570 (Part 5) X04Cr19Ni13Mo3

Strong Match — 87% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31700 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X04Cr19Ni13Mo3 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31700 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr19Ni13Mo3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S31700 vs IS 1570 (Part 5) X04Cr19Ni13Mo3 is a 97.2% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a strong match overall at 87%.

Frequently Compared With ASTM A276/A276M S31700:
ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
97.2%
MECHANICAL MATCH
66.7%
OVERALL
87%
Specifications
Property ASTM A276/A276M S31700 IS 1570 (Part 5) X04Cr19Ni13Mo3
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 18.0-20.0 18.0-20.0
Ni (%) 11.0-15.0 11.0-15.0
Mo (%) 3.0-4.0 3.0-4.0
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31700 IS 1570 (Part 5) X04Cr19Ni13Mo3
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa (0.2 % proof stress)
Elongation >=40% >=35% (50 mm)
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=217 HB; <=95 HRB
Typical Applications
ASTM A276/A276M S31700
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X04Cr19Ni13Mo3
Not documented
Key Differences
Can ASTM A276/A276M S31700 Be Substituted With IS 1570 (Part 5) X04Cr19Ni13Mo3?
ASTM A276/A276M S31700 and IS 1570 (Part 5) X04Cr19Ni13Mo3 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr19Ni13Mo3 is often considered as a substitute for ASTM A276/A276M S31700 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S31700
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr19Ni13Mo3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31700 and IS 1570 (Part 5) X04Cr19Ni13Mo3?
ASTM A276/A276M S31700 specifies N which is not specified for IS 1570 (Part 5) X04Cr19Ni13Mo3.
Can ASTM A276/A276M S31700 be substituted with IS 1570 (Part 5) X04Cr19Ni13Mo3?
ASTM A276/A276M S31700 and IS 1570 (Part 5) X04Cr19Ni13Mo3 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr19Ni13Mo3 is often considered as a substitute for ASTM A276/A276M S31700 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.