ASTM A276/A276M S31727 vs EN 10088-1 1.4006

Minimal Match — 30.4% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31727 (ASTM A276/A276M:2017) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31727 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. ASTM A276/A276M S31727 is defined under ASTM International, originating from United States, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S31727 vs EN 10088-1 1.4006 is a 45.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 30.4%.

Frequently Compared With ASTM A276/A276M S31727:
IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
45.6%
MECHANICAL MATCH
0%
OVERALL
30.4%
Specifications
Property ASTM A276/A276M S31727 EN 10088-1 1.4006
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08–0.15
Mn (%) <=1.00 ≤1.50
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.00 ≤1.00
Cr (%) 17.5-19.0 11.5–13.5
Ni (%) 14.5-16.5 ≤0.75
Mo (%) 3.8-4.5 Not specified
N (%) 0.15-0.21 Not specified
Cu (%) 2.8-4.0 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31727 EN 10088-1 1.4006
Tensile Strength >=550 MPa ≥540 MPa (annealed)
Yield Strength >=245 MPa Not specified
Elongation >=35% ≥18%
Hardness <=217 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
ASTM A276/A276M S31727
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can ASTM A276/A276M S31727 Be Substituted With EN 10088-1 1.4006?
ASTM A276/A276M S31727 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S31727
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
ASTM A276/A276M S31727
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31727 and EN 10088-1 1.4006?
ASTM A276/A276M S31727 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4006.
Can ASTM A276/A276M S31727 be substituted with EN 10088-1 1.4006?
ASTM A276/A276M S31727 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.