ASTM A276/A276M S32053 vs EN 10088-1 1.4401

Minimal Match — 43.1% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32053 (ASTM A276/A276M:2017) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32053 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment. ASTM A276/A276M S32053 is defined under ASTM International, originating from United States, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32053 vs EN 10088-1 1.4401 is a 52.2% match. As per mechanical properties, the match is 25%. Combined, this makes them a minimal match overall at 43.1%.

Frequently Compared With ASTM A276/A276M S32053:
GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
52.2%
MECHANICAL MATCH
25%
OVERALL
43.1%
Specifications
Property ASTM A276/A276M S32053 EN 10088-1 1.4401
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.07
Mn (%) <=1.00 ≤2.00
P (%) <=0.030 Not specified
S (%) <=0.010 Not specified
Si (%) <=1.00 ≤1.00
Cr (%) 22.0-24.0 16.5–18.5
Ni (%) 24.0-26.0 10.5–13.5
Mo (%) 5.0-6.0 2.0–2.5
N (%) 0.17-0.22 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32053 EN 10088-1 1.4401
Tensile Strength >=640 MPa ≥520 MPa
Yield Strength >=295 MPa ≥210 MPa
Elongation >=40% ≥40%
Hardness <=217 HB ≤215 HB
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32053
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can ASTM A276/A276M S32053 Be Substituted With EN 10088-1 1.4401?
ASTM A276/A276M S32053 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S32053
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
ASTM A276/A276M S32053
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32053 and EN 10088-1 1.4401?
ASTM A276/A276M S32053 specifies P, S, N which are not specified for EN 10088-1 1.4401.
Can ASTM A276/A276M S32053 be substituted with EN 10088-1 1.4401?
ASTM A276/A276M S32053 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.