ASTM A276/A276M S32100 vs IS 1570 (Part 5) X04Cr18Ni10Nb

Strong Match — 96.6% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32100 (ASTM A276/A276M:2017) and IS 1570 (Part 5) X04Cr18Ni10Nb (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32100 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr18Ni10Nb is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A276/A276M S32100 vs IS 1570 (Part 5) X04Cr18Ni10Nb is a 94.8% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 96.6%.

Frequently Compared With ASTM A276/A276M S32100:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
94.8%
MECHANICAL MATCH
100%
OVERALL
96.6%
Specifications
Property ASTM A276/A276M S32100 IS 1570 (Part 5) X04Cr18Ni10Nb
Standard ASTM A276/A276M:2017 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Ti (%) <=0.70 Not specified
Nb (%) Not specified >=10xC, <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32100 IS 1570 (Part 5) X04Cr18Ni10Nb
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=183 HB; <=88 HRB
Typical Applications
ASTM A276/A276M S32100
Stainless steel bars and shapes (hot-finished or cold-finished)
IS 1570 (Part 5) X04Cr18Ni10Nb
Not documented
Key Differences
Can ASTM A276/A276M S32100 Be Substituted With IS 1570 (Part 5) X04Cr18Ni10Nb?
ASTM A276/A276M S32100 and IS 1570 (Part 5) X04Cr18Ni10Nb overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Nb is often considered as a substitute for ASTM A276/A276M S32100 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S32100
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr18Ni10Nb
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32100 and IS 1570 (Part 5) X04Cr18Ni10Nb?
ASTM A276/A276M S32100 specifies Ti which is not specified for IS 1570 (Part 5) X04Cr18Ni10Nb. IS 1570 (Part 5) X04Cr18Ni10Nb specifies Nb which is not specified for ASTM A276/A276M S32100.
Can ASTM A276/A276M S32100 be substituted with IS 1570 (Part 5) X04Cr18Ni10Nb?
ASTM A276/A276M S32100 and IS 1570 (Part 5) X04Cr18Ni10Nb overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Nb is often considered as a substitute for ASTM A276/A276M S32100 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.