ASTM A276/A276M S32202 vs EN 10088-1 X2CrNiCuN23-4

Close Alternative — 77.5% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32202 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiCuN23-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32202 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiCuN23-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32202 vs EN 10088-1 X2CrNiCuN23-4 is a 77.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.5%.

Frequently Compared With ASTM A276/A276M S32202:
IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
77.5%
MECHANICAL MATCH
No shared data
OVERALL
77.5%
Specifications
Property ASTM A276/A276M S32202 EN 10088-1 X2CrNiCuN23-4
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=2.00 <=2.00
P (%) <=0.040 <=0.035
S (%) <=0.010 <=0.015
Si (%) <=1.00 <=1.00
Cr (%) 21.5-24.0 22.0-24.0
Ni (%) 1.00-2.80 3.5-5.5
Mo (%) <=0.45 0.10-0.60
N (%) 0.18-0.26 0.05-0.20
Cu (%) Not specified 1.00-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32202 EN 10088-1 X2CrNiCuN23-4
Tensile Strength >=650 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=30% Not specified
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32202
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiCuN23-4
Not documented
Key Differences
Can ASTM A276/A276M S32202 Be Substituted With EN 10088-1 X2CrNiCuN23-4?
ASTM A276/A276M S32202 and EN 10088-1 X2CrNiCuN23-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S32202
0 active listings and RFQs →
EN 10088-1 X2CrNiCuN23-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32202 and EN 10088-1 X2CrNiCuN23-4?
EN 10088-1 X2CrNiCuN23-4 specifies Cu which is not specified for ASTM A276/A276M S32202.
Can ASTM A276/A276M S32202 be substituted with EN 10088-1 X2CrNiCuN23-4?
ASTM A276/A276M S32202 and EN 10088-1 X2CrNiCuN23-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.