ASTM A276/A276M S32506 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32506 (ASTM A276/A276M:2017) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32506 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. ASTM A276/A276M S32506 is defined under ASTM International, originating from United States, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32506 vs EN 10088-1 1.4006 is a 42.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S32506:
GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
42.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A276/A276M S32506 EN 10088-1 1.4006
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08–0.15
Mn (%) <=1.00 ≤1.50
P (%) <=0.040 Not specified
S (%) <=0.015 Not specified
Si (%) <=0.90 ≤1.00
Cr (%) 24.0-26.0 11.5–13.5
Ni (%) 5.5-7.2 ≤0.75
Mo (%) 3.0-3.5 Not specified
N (%) 0.08-0.20 Not specified
W (%) 0.05-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32506 EN 10088-1 1.4006
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
ASTM A276/A276M S32506
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can ASTM A276/A276M S32506 Be Substituted With EN 10088-1 1.4006?
ASTM A276/A276M S32506 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S32506
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
ASTM A276/A276M S32506
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32506 and EN 10088-1 1.4006?
ASTM A276/A276M S32506 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4006.
Can ASTM A276/A276M S32506 be substituted with EN 10088-1 1.4006?
ASTM A276/A276M S32506 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.