Post Stock Login Register

ASTM A276/A276M S32550 vs EN 10088-1 X2CrNiMoN22-5-3

Close Alternative — 77.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32550 (ASTM A276/A276M:2017) and EN 10088-1 X2CrNiMoN22-5-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32550 is defined under ASTM International, originating from United States, while EN 10088-1 X2CrNiMoN22-5-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S32550 vs EN 10088-1 X2CrNiMoN22-5-3 is a 77.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.8%.

Frequently Compared With ASTM A276/A276M S32550:
ASTM A959 255 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 2205 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
77.8%
MECHANICAL MATCH
No shared data
OVERALL
77.8%
Specifications
Property ASTM A276/A276M S32550 EN 10088-1 X2CrNiMoN22-5-3
Standard ASTM A276/A276M:2017 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Mn (%) <=1.50 <=2.00
P (%) <=0.040 <=0.035
S (%) <=0.030 <=0.015
Si (%) <=1.0 <=1.00
Cr (%) 24.0-27.0 21.0-23.0
Ni (%) 4.5-6.5 4.5-6.5
Mo (%) 2.9-3.9 2.50-3.5
N (%) 0.10-0.25 0.10-0.22
Cu (%) 1.50-2.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32550 EN 10088-1 X2CrNiMoN22-5-3
Tensile Strength >=750 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=25% Not specified
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32550
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 X2CrNiMoN22-5-3
Not documented
Key Differences
Can ASTM A276/A276M S32550 Be Substituted With EN 10088-1 X2CrNiMoN22-5-3?
ASTM A276/A276M S32550 and EN 10088-1 X2CrNiMoN22-5-3 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S32550
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN22-5-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32550 and EN 10088-1 X2CrNiMoN22-5-3?
ASTM A276/A276M S32550 specifies Cu which is not specified for EN 10088-1 X2CrNiMoN22-5-3.
Can ASTM A276/A276M S32550 be substituted with EN 10088-1 X2CrNiMoN22-5-3?
ASTM A276/A276M S32550 and EN 10088-1 X2CrNiMoN22-5-3 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.