Post Stock Login Register

ASTM A276/A276M S32750 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32750 (ASTM A276/A276M:2017) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32750 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. ASTM A276/A276M S32750 is defined under ASTM International (United States).

As per chemical composition, ASTM A276/A276M S32750 vs GOST 5632 06Kh23N28 is a 52.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S32750:
ASTM A959 2507 EN 10088-1 1.4401 ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
52.7%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A276/A276M S32750 GOST 5632 06Kh23N28
Standard ASTM A276/A276M:2017 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.06
Mn (%) <=1.20 ≤2.00
P (%) <=0.035 Not specified
S (%) <=0.020 Not specified
Si (%) <=0.80 ≤0.80
Cr (%) 24.0-26.0 22.0–25.0
Ni (%) 6.0-8.0 26.0–29.0
Mo (%) 3.0-5.0 Not specified
N (%) 0.24-0.32 Not specified
Cu (%) <=0.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32750 GOST 5632 06Kh23N28
Tensile Strength >=800 MPa ≥510 MPa
Yield Strength >=550 MPa ≥196 MPa
Elongation >=15% ≥35%
Hardness <=310 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, up to 2 [50.8] incl sizes (first row printed) Not specified
Max Service Temp Not specified 1050°C
Typical Applications
ASTM A276/A276M S32750
Stainless steel bars and shapes (hot-finished or cold-finished)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can ASTM A276/A276M S32750 Be Substituted With GOST 5632 06Kh23N28?
ASTM A276/A276M S32750 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S32750
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
ASTM A276/A276M S32750
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32750 and GOST 5632 06Kh23N28?
ASTM A276/A276M S32750 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can ASTM A276/A276M S32750 be substituted with GOST 5632 06Kh23N28?
ASTM A276/A276M S32750 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.