Post Stock Login Register

ASTM A276/A276M S32760 vs ASTM A959 S39274

Close Alternative — 81.9% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32760 (ASTM A276/A276M:2017) and ASTM A959 S39274 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32760 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S39274 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S32760 is defined under ASTM International, originating from United States, while ASTM A959 S39274 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S32760 vs ASTM A959 S39274 is a 81.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.9%.

Frequently Compared With ASTM A276/A276M S32760:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
81.9%
MECHANICAL MATCH
No shared data
OVERALL
81.9%
Specifications
Property ASTM A276/A276M S32760 ASTM A959 S39274
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.00 <=1.00
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.020
Si (%) <=1.00 <=0.80
Cr (%) 24.0-26.0 24.0-26.0
Ni (%) 6.0-8.0 6.0-8.0
Mo (%) 3.0-4.0 2.5-3.5
N (%) 0.20-0.30 0.24-0.32
Cu (%) 0.50-1.00 0.20-0.80
W (%) 0.50-1.00 1.50-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32760 ASTM A959 S39274
Tensile Strength >=750 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=25% Not specified
Hardness <=310 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32760
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S39274
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S32760 Be Substituted With ASTM A959 S39274?
ASTM A276/A276M S32760 and ASTM A959 S39274 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A276/A276M S32760
0 active listings and RFQs →
ASTM A959 S39274
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32760 and ASTM A959 S39274?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32760 be substituted with ASTM A959 S39274?
ASTM A276/A276M S32760 and ASTM A959 S39274 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.